Nickel 200 and Nickel 201 Plates are commercially pure nickel alloys known for their outstanding resistance to caustic alkalis, excellent ductility, and reliable performance in a broad range of chemical environments.
Nickel 200 provides high thermal and electrical conductivity, while Nickel 201—with reduced carbon content—is specifically designed to resist embrittlement at elevated temperatures.
These plates are widely used in chemical processing, food equipment, synthetic fiber production, electronics, and environments requiring high purity. All materials comply with ASTM B162 / B333 standards and can be supplied in cut-to-size formats with tight dimensional tolerances and optional surface finishing.
| Grade | Ni (%) | C (%) | Cu (%) | Fe (%) | Mn (%) | Si (%) |
|---|---|---|---|---|---|---|
| Nickel 200 | ≥99.0 | ≤0.15 | ≤0.25 | ≤0.40 | ≤0.35 | ≤0.35 |
| Nickel 201 | ≥99.0 | ≤0.02 | ≤0.25 | ≤0.40 | ≤0.35 | ≤0.35 |
| Grade | Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) |
|---|---|---|---|
| Nickel 200 | 380 | 105 | 40 |
| Nickel 201 | 370 | 100 | 45 |
| Form | Thickness | Width | Length |
|---|---|---|---|
| Cold-Rolled Plate | 0.5–6 mm | 1000–1500 mm | 2000–6000 mm |
| Hot-Rolled Plate | 6–100 mm | 1500–2500 mm | 6000–12000 mm |
Material Highlights
Product Features
Nickel 200 and Nickel 201 Plates are commercially pure nickel alloys known for their outstanding resistance to caustic alkalis, excellent ductility, and reliable performance in a broad range of chemical environments.
Nickel 200 provides high thermal and electrical conductivity, while Nickel 201—with reduced carbon content—is specifically designed to resist embrittlement at elevated temperatures.
These plates are widely used in chemical processing, food equipment, synthetic fiber production, electronics, and environments requiring high purity. All materials comply with ASTM B162 / B333 standards and can be supplied in cut-to-size formats with tight dimensional tolerances and optional surface finishing.
| Grade | Ni (%) | C (%) | Cu (%) | Fe (%) | Mn (%) | Si (%) |
|---|---|---|---|---|---|---|
| Nickel 200 | ≥99.0 | ≤0.15 | ≤0.25 | ≤0.40 | ≤0.35 | ≤0.35 |
| Nickel 201 | ≥99.0 | ≤0.02 | ≤0.25 | ≤0.40 | ≤0.35 | ≤0.35 |
| Grade | Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) |
|---|---|---|---|
| Nickel 200 | 380 | 105 | 40 |
| Nickel 201 | 370 | 100 | 45 |
| Form | Thickness | Width | Length |
|---|---|---|---|
| Cold-Rolled Plate | 0.5–6 mm | 1000–1500 mm | 2000–6000 mm |
| Hot-Rolled Plate | 6–100 mm | 1500–2500 mm | 6000–12000 mm |